3024 XR-5®B Fabric
XR® Technology by Seaman Corporation
3024 XR-5B Fabric for Oil Boom Systems
|
|
|
|
|---|---|---|
| Base Fabric Type |
Nylon
|
|
| Base Fabric Weight (nominal) |
6.0 oz/yd2
|
203 g/m2 |
| Coating Type | Elvaloy® based XR-5® compound | |
| Finished Coat Weight ASTM D751 |
24.0 ± 2 oz/yd2 | 814 ± 70 g/m2 |
| Tongue Tear ASTM D751 |
8" x 10" sample@12 in/min 90/70 lbf |
20.3 cm x 25.4 cm sample @30.5 cm/min 401/312 N |
| Grab Tensile ASTM D751 |
600/500 lbf | 2670/2225 N |
| Strip Tensile ASTM D751, Procedure B |
400/300 lbf/in | 356/267 daN/5 cm |
| Adhesion ASTM D751, Dielectric Weld |
10 lbf/in | 9.0 daN/5 cm |
| Hydrostatic Resistance ASTM D751, Procedure A |
500 psi min | 3.45 MPa |
| Low Temperature ASTM D2136 1/8" mandrel, 4 hrs |
Pass @ -30° F | Pass @ -34° C |
| Chemical Resistance ASTM D471 7 day immersion |
Crude Oil: <3% wt loss
Diesel Fuel: <3% wt loss Gasoline: <10% wt loss |
|
| Abrasion Resistance ASTM D3389 Taber Abrasion H-22 wheel, 1000 g load |
Face side: 2,000 cycles, 25.0 mg/100 cycles max. wt. loss
|
|
We believe this information is the best currently available on the subject. We offer it as a suggestion in any appropriate experimentation you may care to undertake. It is subject to revision as additional knowledge and experience are gained. We make no guarantee of results and assume no obligation or liability whatsoever in connection with this information. In case of conflict between standard and metric specifications, standard shall apply.