8218 LTA
XR® Technology by Seaman Corporation
8218 Low Temperature Use Geomembranes
|
|
|
|
|---|---|---|
| Base Fabric Type |
Polyester
|
|
| Base Fabric Weight (nominal) |
3.0 oz/yd2
|
102 g/m2 |
| Coating Type | Flexible PVC | |
| Finished Coated Weight ASTM D751 |
18.0 + 2/-1 oz/yd2 | 610 + 70/-35 g/m2 |
| Tongue Tear ASTM D751 |
8" x 10" sample@12 in/min 100/100 lbf |
20.3 cm x 25.4 cm sample @30.5 cm/min 445/445 N |
| Grab Tensile ASTM D751 |
230/200 lbf | 1024/890 N |
| Strip Tensile ASTM D751, Procedure B |
200/140 lbf/in | 178/125 daN/5 cm |
| Adhesion ASTM D751, Dielectric Weld |
10 lbf/in | 9 daN/5 cm |
| Hydrostatic Resistance ASTM D751, Procedure A |
200 psi | 1.38 MPa |
| Low Temperature ASTM D2136 1/8" mandrel, 4 hr |
Pass @ -67° F | Pass @ -55° C |
| Flame Resistance FTMS 191A, Method 5910 |
Sample not consumed within 2 minutes
|
|
We believe this information is the best currently available on the subject. We offer it as a suggestion in any appropriate experimentation you may care to undertake. It is subject to revision as additional knowledge and experience are gained. We make no guarantee of results and assume no obligation or liability whatsoever in connection with this information. In case of conflict between standard and metric specifications, standard shall apply.