3522 PVC Fabric
XR® Technology by Seaman Corporation
3522 PVC Fabric for Oil Boom Systems
|
|
|
|
|---|---|---|
| Base Fabric Type |
Polyester
|
|
| Base Fabric Weight (nominal) |
6.0 oz/yd2
|
203 g/m2 |
| Coating Type |
Flexible PVC
|
|
| Finished Coat Weight ASTM D751 |
22.0 ± 2 oz/yd2 | 746 ± 70 g/m2 |
| Tongue Tear ASTM D751 |
8" x 10" sample@12 in/min 100/100 lbf |
20.3 cm x 25.4 cm sample @30.5 cm/min 445/445 N |
| Grab Tensile ASTM D751 |
450/450 lbf | 2003/2003 N |
| Strip Tensile ASTM D751 Procedure B |
325/275 lbf/in | 289/245 daN/5 cm |
| Adhesion ASTM D751, Dielectric Weld |
10 lbf/in | 9 daN/5 cm |
| Hydrostatic Resistance ASTM D751, Procedure A |
500 psi | 3.45 MPa |
| Low Temperature ASTM D2136 1/8" mandrel, 4 hrs |
Pass @ -40° F | Pass @ -40° C |
| Chemical Resistance ASTM D471 7 day immersion |
Crude Oil: <15% wt loss
Diesel Fuel: <15% wt loss Gasoline: <25% wt loss |
|
| Flame Resistance FTMS 191A Method 5910 |
Sample not consumed within 2 minutes
|
|
We believe this information is the best currently available on the subject. We offer it as a suggestion in any appropriate experimentation you may care to undertake. It is subject to revision as additional knowledge and experience are gained. We make no guarantee of results and assume no obligation or liability whatsoever in connection with this information. In case of conflict between standard and metric specifications, standard shall apply.