1936 OBU Fabric
XR® Technology by Seaman Corporation
1936 OBU Fabric for Oil Boom Systems
|
|
|
|
|---|---|---|
| Base Fabric Type |
Nylon
|
|
| Base Fabric Weight (nominal) |
13.0 oz/yd2
|
441 g/m2 |
| Coating Type |
Polyether based polyurethane
|
|
| Finished Coat Weight ASTM D751 |
36.0 ± 2 oz/yd2 | 1221 ± 70 g/m2 |
| Tongue Tear ASTM D751 |
8" x 10" sample@12 in/min 85/85 lbf |
20.3 cm x 25.4 cm sample @30.5 cm/min 378/378 N |
| Grab Tensile ASTM D751 |
1150/1150 lbf | 5115/5115 N |
| Strip Tensile ASTM D751, Procedure B |
800/700 lbf/in | 712/623 daN/5 cm |
| Adhesion ASTM D751, Dielectric Weld |
15 lbf/in | 13 daN/5 cm |
| Hydrostatic Resistance ASTM D751, Procedure A |
800 psi | 5.51 MPa |
| Bursting Strength ASTM D751 |
1000 lbf | 4450 N |
| Low Temperature ASTM D2136 1/8" mandrel, 4 hrs |
Pass @ -40° F | Pass @ -40° C |
| Chemical Resistance ASTM D471 7 day immersion |
Crude Oil: <3% wt loss
Diesel Fuel: <3% wt loss Gasoline: <5% wt loss |
|
| Abrasion Resistance ASTM D3389 Taber Abrasion H-22 wheel, 1000 g load |
Face side: 12,000 cycles, 5.0 mg/100 cycles max. wt. loss
|
|
We believe this information is the best currently available on the subject. We offer it as a suggestion in any appropriate experimentation you may care to undertake. It is subject to revision as additional knowledge and experience are gained. We make no guarantee of results and assume no obligation or liability whatsoever in connection with this information. In case of conflict between standard and metric specifications, standard shall apply.