1932 PTF Pillow Tank Fabric
XR® Technology by Seaman Corporation
1932 PTF - Primary and Secondary Containment of
Aromatic Hydrocarbons
|
|
|
|
|---|---|---|
| Base Fabric Type |
Nylon
|
|
| Base Fabric Weight (nominal) |
13.0 oz/yd2
|
441 g/m2 |
| Coating Type | Polyester -base polyurethane | |
| Finished Coated Weight ASTM D751 |
32 ±2 oz/yd2 | 1085 ±70 g/m2 |
| Thickness ASTM D751 |
35 mil (nominal) | 0.89 mm (nominal) |
| Grab Tensile ASTM D751 |
1000/1000 lbf min | 4450/4450 N min |
| Strip Tensile ASTM D751, Procedure B |
600/600 lbf/in min | 526/526 daN/5 cm min |
| Adhesion ASTM D751, Dielectric Weld |
50 lbf/in min | 45 daN/5 cm min |
| Hydrostatic Resistance ASTM D751, Procedure A |
1500 psi min | 10.3 MPa min |
| Bursting Strength ASTM D751, Ball Tip |
1200 lbf min
|
5340 N min |
| Low Temperature ASTM D2136 1/8" mandrel, 4 hrs |
Pass @ -50° F | Pass @ -46° C |
| Dead Load ASTM D751 Pass@ |
2 in seam, 4 hr, 1 in strip 250 lbf @ room temp 125 lbf @ 160° F |
5 cm seam, 4hr, 2.5 cm strip 1113 N @ room temp 556 N @ 71° C |
| Abrasion Resistance ASTM D3389 H-22 wheel/1000g load |
10,000 cycles (min) before fabric exposure |
|
| Permeability ASTM D814 Fuel B |
0.05 fl oz/ft2/24 hr (max) | 15.9 mL/m2/24 hr (max) |
We believe this information is the best currently available on the subject. We offer it as a suggestion in any appropriate experimentation you may care to undertake. It is subject to revision as additional knowledge and experience are gained. We make no guarantee of results and assume no obligation or liability whatsoever in connection with this information. In case of conflict between standard and metric specifications, standard shall apply.